High performance laminating resin. Lower viscosity and longer curing times compared to R240.
Description
KINETIX R246 cures at room temperature, or low elevated temperature, and is suitable for fibre composite construction. The low viscosity of this system is a significant aid in both hand lamination, or machine impregnation, operations.
The relatively low activity of R246 offers extended working times which is also a benefit for large laminating projects.
* In comparison with R240 resin, R246 mixed with associated hardeners, will produce significantly longer working time, typically in the order of 100%.
- Solvent Free
- Room or Low Temperature Cure
- Extended Working Time
- Low Viscosity
Mix ratio: 100 parts resin to 25 parts hardener by weight.
Download Data Sheet here
Additional information
| Weight | N/A |
|---|---|
| Dimensions | N/A |
| Pack Size | Pack C, Pack D |
| Hardener Choice | R246 + Fast H126, R246 + Med H160, R246 Only, Fast H126 (Hardener Only), Med H160 (Hardener Only) |
Hardener comparison
| H126 | H160 | |
| Mix Ratio (Weight) | 100 parts resin to 25 parts hardener | 100 parts resin to 25 parts hardener |
| Mixed Viscosity (larger number is thicker) | 460 mPas | 300 mPas |
| Pot Life (100g @25 deg C) | 40 mins | 120 mins |
| De-mould time | 9 hours 25 min | 28 hours |
| Ultimate heat distortion temperature (After post cure) | 97 deg C | 68 deg C |
| Shore D hardness (larger number is harder) | 79 | 83 |