$165.00 – $895.54 inc GST
High performance laminating resin. Lower viscosity and longer curing times compared to R240. Better hold on vertical surfaces than regular R246.
Description
KINETIX R246TX cures at room temperature, or low elevated temperature, and is suitable for fibre composite construction.
The thixotropic nature of R246TX reduces vertical drainage when high resin contents are employed in heavy laminates.
R246TX offers extended working times and cured mechanical properties are excellent.
* In comparison with R240 resin, R246TX mixed with associated hardeners, will produce significantly longer working time, typically in the order of 100%.
- Solvent Free
- Room or Low Temperature Cure
- Extended Working Time
- Low Viscosity
Mix ratio: 100 parts resin to 25 parts hardener by weight.
Download Data Sheet here
Additional information
| Weight | N/A |
|---|---|
| Dimensions | N/A |
| Pack Size | 5kg, 22.5kg |
| Hardener Choice | Fast H126 1L, Med H160 1L, No Hardener |
Hardener comparison
| H126 | H160 | |
| Mix Ratio (Weight) | 100 parts resin to 25 parts hardener | 100 parts resin to 25 parts hardener |
| Mixed Viscosity (larger number is thicker) | 460 mPas | 300 mPas |
| Pot Life (100g @25 deg C) | 40 mins | 120 mins |
| De-mould time | 9 hours 25 min | 28 hours hours |
| Ultimate heat distortion temperature (After post cure) | 97 deg C | 68 deg C |
| Shore D hardness (larger number is harder) | 79 | 74 |
Download Data Sheet here